Surface functionalization of Al2O3 nano-particles by mussel-inspired poly(dopamine) (PDA) was developed to improve the dielectric properties, mechanical properties, and thermal conductivity properties of nitrile rubber (NBR) matrix. As strong adhesion of PDA to Al2O3 nano-particles and hydrogen bonds formed by the catechol groups of PDA and the polar acrylonitrile groups of NBR, the dispersion of Al2O3-PDA/NBR composites was improved and the interfacial force between Al2O3-PDA and NBR matrix was enhanced. Thus, the Al2O3-PDA/NBR composites exhibited higher dielectric constant, better mechanical properties, and larger thermal conductivity comparing with Al2O3/NBR composites at the same filler content. The largest thermal conductivity of Al2O3-PDA/NBR composite filled with 30 phr Al2O3-PDA was 0.21 W/m K, which was 122% times of pure NBR. In addition, the Al2O3-PDA/NBR composite filled with 30 phr Al2O3-PDA displayed a high tensile strength about 2.61 MPa, which was about 255% of pure NBR. This procedure is eco-friendly and easy handling, which provides a promising route to polymer composites in application of thermal conductivity field. (C) 2018 Elsevier B.V. All rights reserved.