Aluminum doped-zinc oxide (AZO) thin films were prepared on glass substrate by radio-frequency (RF) sputtering at room temperature. The sheet resistance, R-sh [Omega] the resistivity, rho[Omega center dot cm] and the 1/f noise were studied as a function of thickness, t from 50 nm to 450 nm. The eddy current characterized the homogeneity of AZO thin films. The surface morphology has been analysed by atomic force microscopy (AFM). The 1/f noise is normalized with respect to the bias, frequency and unit area, and C-us is proportional to the sheet resistance R-sh. Two configurations were used to characterize material and contact noise. The pressure effect of four point-probe on the material and the contact noise were also investigated. Our results show that the homogeneity of the samples increases as the film thickness increases and the resistivity decreases with increasing thickness and reaches the lowest value of 1 x 10(-3) Omega cm at 450 nm. The average grain size and the root-mean-square roughness increases with rising thickness. The ratio K = C-us / R-sh is proportional to t(2), which indicates that the mobility and the noise parameter alpha(H) shrink with the shrinkage of the thickness.