Journal of Power Sources, Vol.371, 106-111, 2017
Durability and robustness of tubular molten carbonate fuel cells
One anticipated system for high-efficiency power generation is the combination of syngas from gasification and high temperature fuel cells. The system uses a pressurization system, and it takes into account poisoning by impurities in the syngas. The durability and robustness of the fuel cells used in this system are an important issue for commercial applications. This study focuses on tubular molten carbonate fuel cells (MCFCs), which seem to be relatively durable compared with conventional planar-type MCFCs. Various power generation tests were performed in order to evaluate the durability and robustness of the tubular MCFCs. After continuous generation tests at 0.3 MPa, the cell voltage decay rate was found to be 0.8 mV/1000 h at 0.2 A/cm(2). Moreover, it was found to be possible to generate power stably with fuel gas containing 20 ppm H2S. When the differential pressure between the anode and cathode was set to 0.1 MPa, the power generation tests were performed without gas leakage. In addition, starting (heating) and stopping (cooling) could be done in a short period, meaning that the cold start/stop characteristics are favorable. Therefore, the tubular MCFC was confirmed to have the durability necessary for a power generation system.
Keywords:Molten carbonate fuel cell;Tubular type;Li/Na carbonate electrolyte;Pressurization system;Hydrogen sulfide