Intercalated nanocomposites comprised of poly(propylene carbonate) (PPC) and organo-montmorillonite (OMMT) were prepared via a direct melt blending method. The morphological, thermal, rheological, mechanical, and gas barrier properties of composites were carried out in detail. Results of XRD, TEM, and SEM revealed that OMMT dispersed homogeneously in the polymer matrix, and were intercalated by PPC macromolecules. Compared with neat PPC, the PPC/OMMT nanocomposites showed an enhancement in the 5 wt% weight loss temperature (T (-5%)) by near 20 A degrees C with 3 phr OMMT concentration. With the percolation threshold formed, the rheological properties of composites translated from a liquid-like behavior to a solid-like one. Interestingly, PPC/OMMT nanocomposites revealed a concurrent improvement in the modulus, yield strength, and toughness with the addition of homogeneously dispersed clay. The oxygen permeability of well-dispersed PPC/OMMT nanocomposites reduced significantly compared with that of neat PPC. Consequently, this convenient and effective method, which facilitates to prepare PPC/OMMT nanocomposites with superior mechanical properties and excellent gas barrier performances, can be considered to broaden the application of PPC.