Four glass compositions were produced taking into account different theoretical Leucite (KAlSi2O6)/Bioglass 45S5 (45% SiO2, 24.5% Na2O, 24.5% CaO, 6% P2O5) ratios using analytical grade reagents only; and replacing some of the reagents by natural minerals, all that were found to be bioactive when they were transformed to glass ceramics. Glasses of particle size below 174 mu m were wet milled using ethanol in a high energy planetary ball mill. After wet milling, samples with 25 and 30% of theoretical Leucite content using reagents grade raw materials showed a higher dissolution rate in comparison to the same glasses made from natural mineral, while no differences were found on glasses with 40 and 50% of Leucite theoretical content. Samples with higher dissolution showed a crystalline carbonate phase named Pirssonite on its surface, while on the rest of samples amorphous carbonates were present. (C) 2017 Elsevier B.V. All rights reserved.