The clinical success of ceramic restorations is affected by the ceramic bonding procedure. The objective of the study was to evaluate the effect of different surface treatments, including the use of self-etching ceramic primer (SECP), on resin cement-glass ceramic bond strength. Thirty lithium disilicate ceramic (LDC) rectangles (3 mm x 3 mm x 8 mm) were fabricated Specimens were randomly assigned into three experimental groups (n = 10) according to the surface treatment: Group 1-hydrofluoric acid [HF acid]+ silane + universal adhesive; Group 2-HF + universal adhesive; Group 3-SECP + universal adhesive. All specimens were stored in distilled water for 24 h at 37 degrees C and shear bond strength (SBS) was tested at a crosshead speed of 0.5 mm (Universal Testing machine-Instron). Failure modes were evaluated using a digital microscope for all specimens. Analysis of variance and the Tukey post hoc tests using SPSS (Version 22.0, IBM, New York, USA) were used to analyze data. The SBS of groups 1 (19.74 +/- 1.28 MPa) and 3 (21.11 +/- 2.07 MPa) were significant higher than group 2 (14.80 +/- 1.94 MPa). The SBS values for specimens in groups 1 (19.74 +/- 1.28 MPa) and 3 (21.11 +/- 2.07 MPa) were comparable. Adhesive, mixed and cohesive failure modes were observed and mixed failure was the most common in all groups. Therefore, the use of SECP and universal adhesive is recommended as an alternative to the use of HF acid in combination with ceramic primer while bonding to LDC.