In this work, we show the unique wettability properties of TiO2 thin films deposited by e-beam evaporation on glass and treated at 500 degrees C. The deposited materials exhibited compact non-porous structures and their non-UV activated superwetting behavior was characterized, emphasizing the better performance compared to the bare glass substrate and to a commercial self-cleaning glass (Pilkington ActivTM) even in terms of antifogging and optical properties. The results demonstrate how the superhydrophilic character arises from the used deposition technique inducing a large amount of oxygen vacancies further boosted by the annealing treatment, allowing for the fabrication of a pioneering material in the area of multifunctional coatings. The superhydrophilic character was maintained even at an extremely small thickness (20 nm), similarly to the adhesion of the film to the glass substrate, as confirmed by ultrasound stress tests and the cross-cut test performed according to ISO 2409 standard. The photocatalytic activity of the e-beam evaporated film was also assessed by degradation of methanol, 2-propanol and toluene under UV light in a gas phase reactor and the performance was found to be in most cases superior compared to Pilkington Activ (TM). (C) 2017 Elsevier B.V. All rights reserved.