Activated carbons (ACs) based on rice straw (RS) were synthesised using potassium carbonate as activating agent at three different K2CO3/RS weight ratios. Morphological, chemical, structural as well as textural characterisations were carried out in order to establish relationships between the physicochemical properties of the materials and their hydrogen adsorption capacities. The ACs contained potassium and silicon as the main impurities. Si was identified by XRD in both phases of silicon dioxide and silicon carbide. The presence of SiC was particularly surprising due to the rather low activation temperature, much lower than what is usually required for SiC synthesis. ACs exhibited well-developed surface areas (approximatively 2000-2100 m(2) g(-1)) and high micropore volumes, making them suitable for hydrogen storage applications. RS-based ACs showed higher hydrogen storage capacities than those previously obtained with KOH-activated sucrose. The latter exhibited hydrogen uptakes (excess, 10 MPa, 298 K) up to 0.55 wt. %, whereas 0.65 wt. % was measured for RS based ACs in the same conditions. The higher hydrogen capacities and isosteric heats of adsorption found here were attributed to the presence of SiC. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.