Metal supports for planar MS-PCEC were manufactured using tape-casting of low-cost ferritic stainless steel. A coating protecting the metal support against oxidation was applied by vacuum infiltration and a buffer layer of La0.5Sr0.5Ti0.75Ni0.25O3-6 (LSTN) was further deposited to smoothen the surface. The BaZr0.85Y0.15O3-delta-NiO (BZY15-NiO) cathode and the BaZr0.85Y0.15O3-delta (BZY15) electrolyte were applied by pulsed laser deposition (PLD) at elevated substrate temperatures (at 700 degrees C and 600 degrees C, respectively). The main challenges are related to the restrictions in sintering temperature and atmosphere induced by the metal support, as well as strict demands on the roughness of substrates used for PLD. Reduction treatment of the half cells confirmed that NiO in the BZY15-NiO layer was reduced to Ni, resulting in increased porosity of the BZY15-Ni cathode, while keeping the columnar and dense microstructure of the BZY15 electrolyte. Initial electrochemical testing with a Pt anode showed a total resistance of 40 Omega.cm(2) at 600 degrees C. Through this work important advances in using metal supports and thin films in planar PCEC assemblies have been made. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.