Eu2+-activated Ba2ZnS3 has been reported as a red phosphor with a broad emission band peaking at 650 nrn under blue excitation for white-LED. In this study, Ba2ZnS3:Eu2+, X- (X = F, Cl, Br, I) phosphors doped with halide ions were prepared by traditional high temperature solid-state reaction. Phase identification of powders was performed by X-ray powder diffraction analysis, confirming the existence of single-phase Ba2ZnS3 crystals without dopant. The corresponding excitation spectra showed an additional broad band in the green region peaking at 550 nm when the phosphor was halogenated except by the smallest F-. It was proved that the green-excitation efficiency successively strengthened from Cl-, to Br-, to I-, which suggested larger halide ions made a greater contribution to the further splitting of the t(2g) energy level of the doped Eu2+ ions in the host Ba2ZnS3, and the optimized formula Ba1.995ZnS2.82:Eu-0.005(2+), I-0.18(-) showed a potential application in solar spectral conversion for agricultural greenhouse and solar cell. Defect chemistry theory and crystal field theory provided insights into the key role of halide ions in enhancing-green-excitation efficiency.