Here we provide evidence that the principal mechanism responsible for scanning tunneling microscope (STM)-induced removal (or deposition) of material from organic thin films in air is electrochemical in nature. In experiments conducted in high-humidity (>similar to 70% relative humidity) ambients, patterning proceeds at biases above similar to+2.3 V because a thin layer of water adsorbed to the tip and surface establishes an ultra-thin-layer electrochemical cell. The low-energy self-assembled monolayer (SAM) restricts the dimensions of the highly resistive solution in the tip-sample gap and confines the patterning to the immediate vicinity of the tip, passivates unetched regions of the Au(111) substrate, and retards the surface mobility of Au atoms thereby stabilizing the patterns. In the absence of SAMs, patterns in nominally naked Au(lll) are irreproducible and rapidly anneal to their pre-etch form. In low-humidity (

Keywords:TUNNELING-MICROSCOPE OBSERVATION;SELF-ASSEMBLING MONOLAYERS;TIP-INDUCED ANODIZATION;SURFACE-DIFFUSION;AQUEOUS-SOLUTION;GOLD ELECTRODES;SINGLE-CRYSTALS;ATOMIC SCALE;GRAPHITE;AU(111)