The thermal properties of the short carbon fibers (SCFs) filled erythritol phase change composites (PCCs) were investigated experimentally. The samples were prepared with different mass loadings of two kinds of SCFs, 1%, 2%, 4%, 7% and 10%. The melting points and phase change enthalpies were measured by differential scanning calorimeter (DSC). The effects of SCFs on the melting points are relatively small but the enthalpies were reduced with the loadings of SCFs. The greatest loss of enthalpies is 11.3% for composites filled with 10% SCFs. The thermal conductivities increased with the loadings of SCFs but not linearly. The highest thermal conductivity is 3.92 W/(m center dot K) for the composites with 10% longer SCFs, which was enhanced by 407.8% compared to pure erythritol (0.77 W/(m center dot K)). Composites filled with longer SCFs possess higher thermal conductivity and the mechanisms were discussed. A simple setup was made to test the temperature-regulated property of these materials. These include pure erythritol and phase change composites with different loading of SCFs. The PCCs have shown good application potential and the longer SCFs can lead to the better performance of PCCs.(C) 2017 Elsevier Ltd. All rights reserved.