Superamphiphobic Al surfaces were achieved via an easy and environmentally-friendly approach. Aqueous mixed solution of 0.7 M CuSO4 and 1 M NaCl was used to etch polished Al surfaces to fabricate a rough morphology distributed with microscale step-like pits. The uniformly distributed nanoscale petals covered on the microscale pits were obtained by subsequent 96 C-omicron hot deionized water bathing for 13 min. Thus, the hierarchical micro/nanometer scale roughness was formed which provided the structural basic of superamphiphobic Al surfaces. By 1H, 1H, 2H, 2H-Perfluorodecyl-triethoxysilane (PFDTS) derivatization, desirable superamphiphobic Al surfaces were achieved with the highest static contact angles of 162(omicron) for water, 156(omicron) for peanut oil, respectively. Meanwhile, the sliding angles were lower than 10(omicron) for both water and peanut oil droplets. The as-prepared Al surfaces were investigated by field-emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), and optical contact angle measurements. The FE-SEM images of as-prepared Al surfaces showed a hierarchical micro/nanometer scale morphology. XPS analyses demonstrated the PFDTS derivitization on Al surfaces. The superamphiphobic Al surfaces presented good mechanical durability and chemical stability which have a wide range of applications in fields such as self-cleaning, anti-icing, anti-corrosion, oil transportation, energy harvesting, microfluidics, and so forth. The approach reported in this paper may easily realize the industrial production of superamphiphobic Al surfaces owing to the advantage of facile, low cost and environmentally-friendly. (C) 2017 Elsevier B.V. All rights reserved.