Exceptional mechanical and physical properties of transition metal carbides and nitrides make them good coating-material candidates for extreme corrosive environments such as oil and natural gas wells. However, existence of small pores, pinholes and columnar structures of these ceramics significantly affect their resistance to corrosion, as pore sites would accelerate the diffusion of corrosive media into the substrate. In this research, molecular dynamics atomistic simulations are employed to investigate the effects of the isolated vacancies and the columnar structure on the diffusion rate of H atoms in NbC single crystal at various temperatures. Diffusion coefficient (D) of H atoms in NbC increased with C vacancy concentration. At elevated temperatures, the trapping effect of Nb vacancies is less effective when C vacancies are also present, as H atoms gain enough energy to jump back and forth between the C vacancies. Atomistic simulations also showed a jump in diffusion coefficient for cylindrical pore size of larger than 3 A radius. Furthermore, D increased monotonically with temperature up to 1000 K in the presence of cylindrical pores. Further increase in temperature resulted in a drop in the diffusion coefficient for small pores while the large pores only showed a lower increasing trend in diffusion coefficient with the temperature. (C) 2017 Elsevier B.V. All rights reserved.