The effect of particles size ranges (<38 mu m, 75-150 mu m, 270-550 mu m) of atomized magnesium powders on densification mechanisms during spark plasma sintering (SPS) process was investigated. The intrinsic driving force, local pressure and current of Mg powders with different particle sizes were analyzed by theoretical calculation. The results obviously indicate that the densification of pure magnesium can be improved by the reduction of particle size, suggesting the intrinsic driving force, local pressure and current intensity are enhanced significantly by a decrease in the particle size at the same sintering conditions, which can promote shrinkage of pores, formation of the sintering neck and mass transportation in the SPS process. Not only that, rapid densification is also interpreted in term of mechanical movement of particles, Joule heating effect and plastic deformation. However, the mechanical movement of the large particles is higher than that of small particles due to high punch displacement, and plastic deformation, detected by scanning electron microscopy, plays a main role in densification for large particles in the case during the sintering. Joule heating effect is the key factor for densification of small Mg particles, and high densification degree can be obtained by sintering small particles. (C) 2017 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.