This work presented a novel phosphorus and sulfur dual doped porous carbon materials (PSDPC) with hierarchic porous structure, large specific surface area and extra-large pore volume fabricated using phytic acid as precursor and SBA-15 as template. The specific surface areas and total pore volume of the reported materials reached 2276 m(2) g(-1) and 3.95 cm(3) g(-1), respectively. The P and S heteroatoms were successfully incorporated into the framework of the carbon matrix mainly by P-C bond and thiophenelike sulfur species, doping level was found to be 1.88 and 1.23 at.% for P and S heteroatoms, respectively. The reported material exhibited competitive electric storage/release capacity, excellent rate capability and good cycle performance, which specific capacitance reached 253 Fg(-1), no apparent decrease of the specific capacitance was observed as the current density increased from 0.5 to 10 Ag-1, and the specific capacitance retention reached 100% after 1000 times charge/discharge cycle. (C) 2016 Elsevier Ltd. All rights reserved.