LiF-NiO composites in a molar ratio of 1:1 are synthesized by the mechanical milling of equal amounts of LiF and NiO for 12-144 h. The synthesized composites are investigated by XRD, charge-discharge measurements, and XPS. The XRD peaks of NiO broaden with an increase in the milling time, while those of LiF disappear. Rietveld analysis shows that the LiF-NiO composites prepared by milling for more than 72 h form a solid solution and that the arrangement of Li+ and Ni2+ ions in them is disordered. The LiF and NiO samples milled individually do not exhibit a noticeable discharge capacity, while the composites show a large one. Further, the discharge capacity of the LiF-NiO composites increases with the milling time, with the composite prepared by milling for 144 h exhibiting a discharge capacity of 216 mA h g(-1) and an average voltage of 3.53 V at 0.05 C for voltages of 2.0-5.0 V. The XPS data suggest that the Ni ions are probably oxidized and reduced repeatedly during the charge-discharge process and that the Ni2+ ions are partially oxidized to Ni3+ ions during charging to 5.0 V. (C) 2016 Elsevier B.V. All rights reserved.