This study reports on the dependence of the temperature-induced changes in the properties of thin thermoresponsive poly(diethylene glycol) methyl ether methacrylate (PDEGMA) layers of end-tethered chains on polymer thickness and grafting density. PDEGMA layers with a dry ellipsometric thickness of 5-40 nm were synthesized by surface-initiated atom transfer radical polymerization on gold. To assess the temperature-induced changes, the adsorption of bovine serum albumin (BSA) was investigated systematically as a function of film thickness, temperature, and grafting density by surface plasmon resonance (SPR), complemented by wettability and quartz crystal microbalance with dissipation monitoring (QCM-D) measurements. BSA adsorption on PDEGMA brushes is shown to differ significantly above and below an apparent transition temperature. This surface transition temperature was found to depend linearly on the PDEGMA thickness and changed from 35 degrees C at 5 nm thickness to 48 degrees C at 23 nm. Similarly, a change of the grafting density enables the adjustment of this transition temperature presumably via a transition from the mushroom to the brush regime. Finally, BSA that adsorbed irreversibly on polymer brushes at temperatures above the transition temperature can be desorbed by reducing the temperature to 25 degrees C, underlining the reversibly switchable properties of PDEGMA brushes in response to temperature changes.