A presynthesized, square planar copper imidazole complex, [Cu(imidazole)(4)](NO3)(2), was utilized as a precursor in the synthesis of a new series of zeolitic imidazolate frameworks, termed ZIF-202, -203, and -204. The structures of all three members were solved by single-crystal X-ray diffraction analysis, which revealed ZIF-203 and -204 having successfully integrated square planar units within the backbones of their respective frameworks. As a result of this unit, the structures of both ZIF-203 and -204 were found to adopt unprecedented three-dimensional nets, namely, ntn and thl, respectively. One member of this series, ZIF-204, was demonstrated to be highly porous, exhibit exceptional stability in water, and selectively capture CO2 over CH4 under both dry and wet conditions without any loss in performance over three cycles. Remarkably, the regeneration of ZIF-204 was performed under the mild conditions of flowing a pure N-2 gas through the material at ambient temperature.