The colloidal stability together with the tunable aggregation and viscoelastic properties of thermoresponsive polymer grafted cellulose nanocrystals (CNCs) were investigated. TEMPO oxidation of CNCs followed by peptidic coupling in water were used to covalently graft thermosensitive Jeffamine polyetheramine M2005 chains onto the surface of CNCs. The resulting polymer-decorated particles (M2005-g-CNCs) exhibited new colloidal properties, by their ability to perfectly redisperse in water and organic solvents such as toluene, dichloromethane or DMF after freeze-drying. In addition, they presented an enhanced thermal stability when compared to that of sulfated or TEMPO-oxidized CNCs. Dynamic light scattering experiments were used to demonstrate that the thermally induced aggregation of M2005-g-CNCs was fully reversible and reproducible over many temperature cycles and that, most interestingly, the aggregation number could be tuned by varying the ionic strength and/or the pH of the medium, making the suspension multiresponsive. This property arises from the variations of the sign (attractive or repulsive) and the range of the different types (entropic, electrostatic, hydrophobic) of interaction forces between the thermosensitive polymer-decorated nanoparticles. The variation of the viscoelastic properties of M2005-g-CNCs suspensions as a function of temperature, probed by oscillatory rheology measurements of more concentrated suspensions, revealed a reversible temperature-triggered liquid-to-gel transition. Such enhanced functionalities pave the way to the design of advanced CNC-based materials benefiting both from the intrinsic characteristics of these biosourced particles and the new properties imparted by the stimuli-sensitive grafted chains.