A series of waterborne polyurethane (WPU) containing alkoxysilane side groups were synthesized by using the dihydroxy functionalized alkoxysilane. The diol with trimethoxysilane groups at the side chains was synthesized via Michael addition between 3-(methacryloxypropyl)trimethoxysilane (MAPTS) and diethanolamine (DEA). The silane diol was applied as the chain extender for the NCO-endcapped prepolymer of isophorone diisocyanate, polycarbonate diol, 2,2-bis(hydroxymethyl) butyric acid and 1,4-butanediol. The products with the silane content varied from 1.2 to 16.5 wt% were dispersed in water after neutralization. The effect of the silane diol on the particle size and morphology of the WPU dispersion was studied by dynamic light scattering (DLS) and transmission electron microscopy (TEM), respectively. X-ray photoelectron spectroscopy (XPS) characterization was carried out on the coating film of the WPU, revealing that the long flexible side chain is favorable for the silane components to emigrate toward the film surface and crosslink during the film formation process. As a result, both the surface contact angle to water and water adsorption of the WPU coating films increased with the silane content. Furthermore, the mechanical properties including the modulus and tensile strength of the films were also improved by the incorporation of silane diol. (C) 2016 Elsevier B.V. All rights reserved.