The surface of indigenous aramid fiber-3 (IAF3) was decorated via mutual irradiation grafting process in diethanolamine (DEA) and epichlorohydrin (ECH), respectively, with the assist of high energy gamma rays. This modification method with great permeability produced the homogeneous and ameliorative AF3 surfaces, which were observed by the scanning electron microscopy (SEM) and atom forced microscopy (AFM). Enhanced surface free energy and reduced contact angles of irradiated AF3 verified the fabulous effectiveness of mutual irradiation without seriously injured tensile strength. The composites based on epoxy resin (ER) polymer as the matrix and irradiated IAF3 grafted DEA and ECH as the reinforcement. By capitalizing on the irradiated IAF3 which has higher wettability and adsorption on resin, the irradiated IAF3-ECH/ER composites exhibit admirable interfacial mechanical performance as compared to the pristine IAF3 contained composites. The interfacial shear strength (IFSS), interlaminar shear strength (ILSS) and flexural strength of composites were remarkable improved to 86.5, 60.13 and 511 MPa respectively, from the pristine IAF3/ER composite with IFSS of 65.9 MPa, ILSS of 48.1 MPa, and flexural strength of 479 MPa. (C) 2016 Elsevier B.V. All rights reserved.