An experimental procedure to coat superelastic NiTi alloys with flexible TiO2 protective nanocomposite films using sol-gel technology was developed in this work to improve the metal biocompatibility without deteriorating its superelastic mechanical properties. The coatings were characterized by scanning and transmission electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy, and glazing incidence X-ray diffraction. The elasticity of the film was tested in coated specimens submitted to three-point bending tests. A short densification by thermal treatment at 500 degrees C for 10 min yielded a bilayer film consisting of a 50 nm-thick crystallized TiO2 at the inner interface with another 50-nm-thick amorphous oxide film at the outer interface. This bilayer could sustain over 6.4% strain without cracking and could thus be used to coat biomedical instruments as well as other devices made with superelastic NiTi alloys. (C) 2016 Elsevier B.V. All rights reserved.