The role of the stability of surface functional groups in oxygen- and nitrogen-functionalized multi-walled carbon nanotubes (CNTs) applied as support for iron catalysts in high-temperature Fischer-Tropsch synthesis was studied in a fixed-bed U-tube reactor at 340 degrees C and 25 bar with a H-2:CO ratio of 1. Iron oxide nanoparticles supported on untreated oxygen-functionalized CNTs (OCNTs) and nitrogen-functionalized CNTs (NCNTs) as well as thermally treated OCNTs were synthesized by the dry impregnation method using ammonium ferric citrate as iron precursor. The properties of all catalysts were examined using X-ray diffraction, temperature-programmed reduction in H-2, X-ray photoelectron spectroscopy and temperature-programmed oxidation in O-2. The activity loss for iron nanoparticles supported on untreated OCNTs was found to originate from severe sintering and carbon encapsulation of the iron carbide nanoparticles under reaction conditions. Conversely, the sintering of the iron carbide nanoparticles on thermally treated OCNTs and untreated NCNTs during reaction was far less pronounced. The presence of more stable surface functional groups in both thermally treated OCNTs and untreated NCNTs is assumed to be responsible for the less severe sintering of the iron carbide nanoparticles during reaction. As a result, no activity loss for iron nanoparticles supported on thermally treated OCNTs and untreated NCNTs was observed, which even became gradually more active under reaction conditions. (C) 2015 Published by Elsevier B.V.