Disc type ceramic aluminium oxide membrane has been prepared by tape casting technique. Thickness of this single layer membrane is in the range 200-300 mu m. Porosity and pore size distribution have been determined by mercury porosimetry. Polymeric binder content of the green tape and the firing temperature are found to have strong influence on the average pore size, pore size distribution and overall porosity. Higher binder content promotes agglomeration of the ceramic particles, which on firing leads to wider pore size distribution and formation of closed pores. Pore coarsening is observed with increasing firing temperature.