Heterogeneous photocatalysis using TiO2 can effectively remove antibiotics from water using UV light; however, its performance is notably reduced under sunlight irradiation. The use of metallic nanoparticles deposited on TiO2 may result in the photo-activation of the catalyst within the visible spectrum. In this study mono- (Au, Ag and Cu) and bi-metallic Au-Ag and Au-Cu nanoparticles were deposited on TiO2 to photocatalytically degrade the antibiotic ciprofloxacin in pure water using either UV-C or simulated sunlight. The optimal loading of mono-metallic nanoparticles on TiO2 was determined as 1.5 wt.% for Au and Ag, and 1.0 wt.% for Cu; first order degradation rates (k(app)) of 0.06, 0.117 and 0.072 min(-1), respectively, were determined for these materials. In UV-C tests, the complete degradation of ciprofloxacin was achieved upon 90 min of irradiation, whilst complete mineralization was reached in <180 min for all of the tested catalysts. In simulated sunlight photocatalysis, ciprofloxacin was only partially removed upon 360 min of irradiation when using mono-metallic materials, while complete mineralization was achieved when bi-metallic nanoparticles on TiO2 were tested. A group of by-products were identified and degradation paths were elucidated for photolysis and photocatalysis. Toxicity tests using V. fischeri showed the non-toxicity of the by-products remaining after 360 min of simulated sunlight irradiation. Even though toxicity was low, ciprofloxacin by-products showed some residual antibiotic activity. No catalyst deactivation was observed after 3 consecutive reaction cycles. (C) 2015 Elsevier B.V. All rights reserved.