We investigated crystallinity parameters and ordering domains of poly(3-hexylthiophene-2,5-diyl) blended in [6,6]-phenyl-C-61-butyric acid methyl ester films, which were fabricated by pulsed electrospray deposition methods. The crystallinity parameter and the ordering domain were estimated from Raman and optical absorption spectra, respectively. As a result, they were improved with decreasing the off time of pulse voltage, corresponding to the slow evaporation speed of solvent. In addition, both the space-charge limited current mobility and the photoconversion efficiency showed same trend. A highest photoconversion efficiency of 1.11 % was achieved without the thermal annealing process after depositing the active layer.