Polyaniline nanorods ( PANI-NR) were synthesized by the template free method. The diameter and length of PANI-NR was approximately 120 similar to 200nm and 600 similar to 1200 nm, respectively. PANI-NR= cyanoresin blends were prepared by the addition of cyanoresin= dimethylformamide ( DMF) solutions to PANI- NR= DMF solutions. The conductivity of PANI- NR= cyanoresin blends was in the range of 10(-3) similar to 10(-1) S/cm depending on the cyanoresin content. Thermal stability of PANI- NR/cyanoresin blend was improved with increasing cyanoresin content.