Pb0.92La0.08(Zr0.52Ti0.48)(0.98)O-3 (PLZT) thin films were prepared by chemical solution deposition with varying ligand concentrations. The effects of ligand concentration on structural, ferroelectric and piezoelectric properties of PLZT films were studied. Ethylene glycol was used as chelating ligand and the concentration was varied by taking ligand to solvent volumetric ratios 1:1, 1:2 and 1:3. Change in concentration of the ligand had shown profound effect on phase formation and microstructure leading to an improvement in ferroelectric and piezoelectric properties. Maximum polarization (59.6 mu C/cm(2)) and d(33) (420 pm/V) was achieved for ligand to solvent ratio 1:1 which is considered as an optimum concentration ratio. (C) 2015 Elsevier B.V. All rights reserved.