Cr-containing stainless steels are widely used as metallic interconnects for SOFCs. Volatile Cr-containing species, which originate from the oxide formed on steel, can poison the cathode material and subsequently cause degradation in the SOFC stack. Mn1.5Co1.5O4 spinel is one of the most promising coating materials due to its high electrical conductivity, good CTE match with the stainless steel substrate and an excellent chromium retention capability. In this work Mn1.5Co1.5O4 spinel coatings are deposited on Crofer22APU substrates by cathodic electrophoretic deposition (EPD) followed by sintering at 800 -1150 degrees C in different atmospheres. Dense, continuous and crack free Mn1.5Co1.5O4 coatings (with thickness ranging from 10 to 40 gm) are obtained on Crofer22APU substrates. Moreover, electrical properties of the coated Crofer22APU alloy are tested up to 2500 h and an excellent compatibility is found between Mn1.5Co1.5O4 coated Crofer22APU and a new glass-ceramic sealant, after 500 h of thermal tests in air, thus suggesting that the spinet protection layer can effectively act as a barrier to outward diffusion of Cr. (C) 2015 Elsevier B.V. All rights reserved.