In this study, acidified lithium ion-sieves (HMOs) containing unique inner ionic channels suitable for the transfer of H5 are selected as proton-conductive fillers to prepare hybrid membranes for the first time. By using facile distillation-precipitation polymerization process, two types of sulfonated HMOs (SHM05) are prepared: L-SHM05, which are modified by sulfonate polyelectrolyte layer, and B-SHM05, which are sulfonate polyelectrolyte brushes. The results demonstrate that these fillers improve the thermal and mechanical stabilities of chitosan (CS) control membranes. The incorporation of pristine HMOs enhances the water uptakes and proton conduction abilities of hybrid membranes at suitable loading. By comparison, SHMOs-filled membranes possess higher proton conductivities than those of HMO-filled membranes, owing to the additional proton hopping sites of-So(3)H and acid-base pairs (-SO3- center dot center dot center dot +3HN-). Moreover, B-SHMO-filled membranes exhibit superior proton conductivities over LSHMO-filled ones, demonstrating that the polymer brushes on HMOs allow more-So(3)H groups to form acid-base pairs with CS chains. Particularly, CS/B-SHMO-12 obtains the highest hydrated and anhydrous conductivities of 0.0224 S cm-1 and 10.03 mS cm(-1), enhancing by 91.4% and 98.6% respectively compared with those of CS control membrane under identical conditions. The enhanced proton conductivities offer SHMO-filled membranes elevated cell performances. (C) 2015 Elsevier B.V. All rights reserved.