This study examines adsorption of CO2 and CH4 gases and CO2/CH4 selectivity on titanium based MOFs such as MIL-125(Ti), NH2-MIL-125(Ti) and MIX-MIL-125(Ti) at high pressures up to 10 bar. Characterization and structural analysis of the samples were studied using FT-IR, XRD, TGA, SEM and N-2 adsorption/desorption. The effects of double linkers in the synthesis process and addition of amino-functionalised linker in the structure on adsorption of CO2 and CH4 have been discussed. It was found that addition of NH2 functional group will increase surface area and micropore volume, but reduce particle size. Meanwhile, both CO2 and CH4 adsorption will also be increased. Using binary linkers, thermal stability of MIX-MIL-125(Ti) will also be improved. NH2-MIL-125(Ti) showed the highest CO2 and CH4 adsorption capacities. The adsorption heats of CO2 on MIL-125(Ti), NH2-MIL-125(Ti) and MIX-MIL-125(Ti) were not changed significantly, while the adsorption heats of CH4 reduced after amino functionalization. The selectivity factor of CO2/CH4 in MIX-MIL-125 was lower than MIL-125 but higher than NH2-MIL-125. Compared with other adsorbents such as other MOFs, zeolite 13X and activated carbon, MIL-125 demonstrated a higher selectivity factor. (C) 2015 Elsevier Ltd. All rights reserved.