The effects of vanadium inclusions on the magnetic properties of non-oriented electrical steel sheets were investigated. The magnetic induction and core loss of test specimens deteriorated at a vanadium content of 0.016 wt %. Electron microscope study revealed that the deterioration was caused by the "pinning effects" of vanadium carbonitrides on the recrystallization of cold-rolled sheets.