Patterned fluorine-doped tin oxide electrodes for dye-sensitized solar cells were fabricated by a facile wet etching method. The pattern depth could be controlled by altering etching time. Most dye-sensitized solar cells with patterned fluorine-doped tin oxide electrodes exhibited larger photocurrents. The energy conversion efficiency gradually increased with increasing etching time and obtained a maximum of 7.71% when etching time was 240 s. Then it dropped abruptly if etching duration was more prolonged. An optimum pattern depth is required to achieve the highest performance. The improved performance could be mainly attributed to enhanced light harvesting and scattering due to larger amount of titanium dioxide nanoparticles filled in the circular pattern leading to more dye adsorption. The charge transfer impedance at the titanium dioxide/electrolyte interface also affected the performance of dye-sensitized solar cells. By appropriate etching for surface patterning of fluorine-doped tin oxide electrodes, the device performance had a 16% improvement, which was more efficient than merely adding layer of titanium dioxide nanoparticles on non-patterned fluorine-doped tin oxide. (C) 2015 Elsevier Ltd. All rights reserved.