Non-precious metal electrodes, Ni and Co hydroxides and oxides, have been recently found active towards electro-oxidation of methanol in alkaline. In this article, we present a first and complete study on composition dependence of Ni-Co hydroxides and oxides for methanol electro-oxidation. Ni-Co hydroxide electrodes were prepared by co-electrodeposition on stainless steel mesh (SSM). The atomic ratio of Ni/ Ni + Co in Ni-Co hydroxides was controlled by adjusting the ratio of precursor concentration. Ni-Co oxide electrodes were further obtained by annealing the Ni-Co hydroxides. The morphology factors of Ni-Co hydroxides and oxides were revealed by measuring double layer capacitance using cyclic voltammetry (CV). Methanol oxidation reaction (MOR) performance of these Ni-Co hydroxides and oxide electrodes was investigated by CV, and electrochemical impedance spectroscopy (EIS) techniques at room temperature (RT, similar to 25 degrees C). It is found that the MOR performance of Ni-Co hydroxides increased with the increase of Ni content, while the performance of Ni-Co oxide electrodes presented a volcano plot. The highest MOR performance, the smallest charge transfer resistance and Tafel slope were found at the atomic composition of 46% Ni. Such an enhancement probably was due to the synergistic effect of coexisting Ni and Co in the spinel structure. In contrast, the electrode with the mixture of Ni oxide and Co oxide was unable to reach such a high activity. The function of Ni in Ni-Co hydroxides and oxides was attributed to facilitating the methanol oxidation, and in low potential it presented high absorption of intermediate products. (C) 2015 Elsevier Ltd. All rights reserved.