Rh modified Au(111-25 nm) electrodes, prepared by electron beam evaporation and galvanostatic deposition, were employed to study adsorption and electro-oxidation of CO on Rh in 0.1 M sulfuric acid solution by in situ attenuated total reflection surface enhanced infrared absorption spectroscopy (ATR-SEIRAS). The results of ATR-SEIRAS experiments were compared with those obtained by infrared reflection absorption spectroscopy on three low-index Rh single crystal surfaces. The Rh film deposited on Au(111-25 nm) electrode consists of 3D clusters forming a highly stepped [n(111) x (111)]-like surface with narrow (111) terraces. When CO was dosed at the hydrogen adsorption potential region, CO adsorbed in both atop (COL) and bridge (COB) configurations, as well as coadsorbed water species, were detected on the Rh film electrode. A partial interconversion of spectroscopic bands due to the CO displacement from bridge to atop sites was found during the anodic potential scan, revealing that there is a potential-dependent preference of CO adsorption sites on Rh surfaces. Our data indicate that CO oxidation on Rh electrode surface in acidic media involves coadsorbed water and follows the nucleation and growth model of a Langmuir-Hinshelwood type reaction. (C) 2015 Elsevier Ltd. All rights reserved.