Laser-induced surface and structural modification of silicon (Si) has been investigated under three different environments of vacuum, nitrogen (100 Torr) and ethanol. The interaction of 1000 pulses of KrF (lambda approximate to 248 nm, tau approximate to 18 ns, repetition rate approximate to 30 Hz) Excimer laser at two different fluences of 2.8 J/cm(2) and 4 J/cm(2) resulted in formation of various kinds of features such as laser induced periodic surface structures (LIPSS), spikes, columns, cones and cracks. Surface morphology has been observed by Scanning Electron Microscope (SEM). Whereas, structural modification of irradiated targets is explored by Raman spectroscopy. SEM analysis exhibits a non-uniform distribution of micro-scale pillars and spikes at the central ablated regime of silicon irradiated at low laser fluence of 2.8 J/cm(2) under vacuum. Whereas cones, pits, cavities and ripples like features are seen at the boundaries. At higher fluence of 4 J/cm(2), laser induced periodic structures as well as micro-columns are observed. In the case of ablation in nitrogen environment, melting, splashing, self-organized granular structures and cracks along with redeposition are observed at lower fluence. Such types of small scaled structures in nitrogen are attributed to confinement and shielding effects of nitrogen plasma. Whereas, a crater with multiple ablative layers is formed in the case of ablation at higher fluence. Significantly different surface morphology of Si is observed in the case of ablation in ethanol. It reveals the formation of cavities along with small scale pores and less redeposition. These results reveal that the growth of surface and morphological features of irradiated Si are strongly dependent upon the laser fluence as well as environmental conditions. The difference in surface morphology is attributable to cooling, confinement and shielding effects as well as difference in plasma temperature, density and pressure of environmental media that corresponds to different energy deposition to the target surface. Raman spectroscopy shows that no new bands are identified in case of ablation in all three environments. However, a significant Raman shift is observed which is attributed to laser-induced stresses. (C) 2015 Elsevier B.V. All rights reserved.