In the present study, monodisperse colloidal zinc oxide (ZnO) nanospheres were successfully synthesized via a newly developed two-stage solution method followed by facile calcination at various temperatures. The effects of calcination temperature on the structure, morphology, and optical properties as well as the photocatalytic activity of the as-made ZnO samples were investigated systematically by Fourier transform infrared spectrometry, X-ray diffraction, field emission scanning electron microscopy, nitrogen adsorption/desorption isotherms, diffuse reflectance UV-visible spectroscopy (DRS), photoluminescence, and related photocatalytic activity tests. The thermal decomposition was analyzed by thermogravimetric analysis. The crystallinity was found to gradually increase with increasing calcination temperature, whereas the decrease in the Brunauer-Emmett-Teller specific surface area of the samples with calcination may be ascribed to the increased particle size. The DRS results provided clear evidence for the decrease in band gap energy of ZnO samples with an increase in calcination temperature. The photoluminescence spectra demonstrated the calcination-dependent emission features, especially the UV emission intensity. In particular, the ZnO product calcined at 400 degrees C exhibited the highest photocatalytic activity, degrading methylene blue by almost 99.1% in 70 min, which is ascribed to the large specific surface area and pore volume, high electron-hole pair separation efficient, and great redox potential of the obtained ZnO nanoparticles. In addition, the production of photogenerated hydroxyl radicals (center dot OH) was consistent with the methylene blue degradation efficiency over the as-made ZnO nanoparticles. Using isopropanol as a hydroxyl radical scavenger, center dot OH was determined to be the main active oxygen species in the photocatalytic process. A possible mechanism of photodegradation under UV light irradiation also is proposed. (C) 2015 Elsevier B.V. All rights reserved.