Floating catalyst chemical vapor deposition (FCCVD) has been widely used for the growth of various carbon nanotube (CNT) macrostructures, mainly including vertically aligned CNT (VACNT) arrays and none-woven CNT films. However, it is still unclear for the reason why these CNT macrostructures with largely different morphologies were received via the similar method. In this research, it revealed that the growth temperature largely affected the nucleation status of floating catalysts and thus controlled the morphologies of CNT macrostructures from VACNT arrays to none-woven CNT films. In low temperatures (below 800 degrees C), VACNTs were grown by bottom-up mechanism with several CNTs, but not one individual from bottom to up along the array height direction. Furthermore, VACNT arrays were only grown on some substrates that can induce iron atoms aggregating to catalyst particles with a suitable size. When increasing the growth temperature higher than 800 degrees C, more catalyst particles were nucleated in the gas flow, which induced the formation of none-woven CNT films composed of thin CNTs (single-walled CNTs and double-walled CNTs). This research was significative for understanding CNT growth mechanism via FCCVD process and the synthesis of different CNT macrostructures by this strategy. (C) 2015 Elsevier B.V. All rights reserved.