The 8mol.%Y 2 O 3 - ZrO 2 mainly employed as an electrolyte of solid oxide fuel cells(SOFCs) shows excellent electrical properties but has a weakness in the mechanical properties. Since the electrolyte of SOFCs requires both good electrical and mechanical properties, this study was conducted to meet both requirements. The electrolyte thin films were produced on the LSM(cathode material) substrate of a cell and Si wafer. Four electrolyte film types of single layer and the multiple layer, consisting of 3-YSZ(3mol.% Y 2 O 3 ) with excellent mechanical properties and 8-YSZ with the excellent electric conduction, were produced by electron beam coating technology. Ther crystal structure and the mechanical properties were also analysed. As the results of the study, the 3-YSZ thin film turned out to be in the tetragonal, partially monoclinic phase, while the 8-YSZ thin film showed the cubic phase. The residual stress in the multiple layer was lower than that of the single layer. The microhardness of the multiple layer was similar to that of the existing 8-YSZ single layer both before and after annealing treatment.