The influence of assembled time on the corrosion behaviors of SAMs film on the AM60B alloy and its assembled mechanism have been investigated by electrochemical measurements, scanning electron microscopy (SEM) observation and X-ray photoelectron spectroscopy (XPS) analysis. The self-assembled experiment on the AM60B magnesium alloy indicates that the corrosion susceptibility decreases with increasing assembled time until 24 h on cast AM60B alloy and then increases with increase of the assembled time proved by EIS measurement and potentiodynamic curves. The self-assembled experiments on pure magnesium and various heat treated cast AM60B magnesium alloy illuminate that the dissolved aluminum in magnesium solid solution is the key factor for assembled efficiency and is hard to self-assemble on the pure magnesium without aluminum. The corrosion resistance of self-assembled film on AM60B magnesium alloy is monotonically increasing with the dissolved aluminum. The results of XPS analysis reveal the assembled mechanism on AM60B and corroborate the function of Al element. (C) 2014 Elsevier B.V. All rights reserved.