Porous graphitic carbons were obtained from wood precursors using Ni as a graphitization catalyst during pyrolysis. The structure of the resulting material retains that of the original wood precursors with highly aligned, hierarchical porosity. Thermal characterization was performed by means of thermogravimetry and differential scanning calorimetry, and the onset temperature for graphitization was determined to be similar to 900 A degrees C. Structural and microstructural characterization was performed by means of electron microscopy, electron and x-ray diffraction, and Raman spectroscopy. The effect of maximum pyrolysis temperature on the degree of graphitization was assessed. No significant temperature effect was detected by means of Raman scattering in the range of 1000-1400 A degrees C, but at temperatures over the melting point of the catalyst, the formation of graphite grains with long-range order was detected.