Municipal solid waste incineration bottom ash (MSWI-BA) glass serves as a matrix of assorted bottom ash (BA) compounds. Deterioration of the BA glass phases is quite important as they regulate the distribution of a series of toxic elements. This paper studied landfilled MSWI-BA samples from the mineralogical and geochemical viewpoint to understand the deterioration behavior of the BA glass phases as well as mechanisms involved. Bulk analysis by PXRD as well as micro-scale analysis by optical microscopy and SEM/EDX was conducted for such purposes. The results revealed that dissolution of the BA glass phases has resulted in a deterioration layer of 10(0)-10(2) mu m thickness after years of disposal. This rapid weathering process is highly relevant to the specific glass characteristics and solution pH. The BA glass phases with more embedded compounds and cracks/fissures tend to be more vulnerable. Moreover, the generally alkaline pH in ash deposit favors a rapid disruption of the glass phase. The weathering products are mainly gel phases (including Al-Si gel, Ca-Al-Si gel, Fe-Al-Si gel etc.) with iron oxide/hydroxide as accessory products. Breakdown of the BA glass phases triggers chemical evolution of the embedded compounds. Based on all the findings above, a model is proposed to illustrate a general evolution trend for the landfilled MS WI-BA glass phases. (C) 2014 Elsevier B.V. All rights reserved.