The synthesis, crystal structure, magnetic properties, and europium Mossbauer spectroscopy of the new members of the 9-4-9 Zintl family of Eu9Cd4-xCM2+x-y square ySb9 (CM = coinage metal: Au, Ag, and Cu) are reported. These compounds crystallize in the Ca9Mn4Bi9 structure type (9-4-9) with the 4g interstitial site almost half-occupied by coinage metals; these are the first members in the 9-4-9 family where the interstitial positions are occupied by a monovalent metal. All previously known compounds with this structure type include divalent interstitials where these interstitials are typically the same as the transition metals in the anionic framework. Single-crystal magnetic susceptibility data indicate paramagnetic behavior for all three compounds with antiferromagnetic ordering below 10 K (at 100 Oe) that shifts to lower temperature (<7 K) by applying a 3 T magnetic field. 151Eu Mossbauer spectra were collected on polycrystalline powder samples of Eu9Cd4-xCM2+x-y square ySb9 at 50 and 6.5 K in order to evaluate the valence of Eu cations. Although the Zintl formalism states that the five crystallographically distinct Eu sites in Eu9Cd4-xCM2+x-y square ySb9 should bear Eu2+ , the Mossbauer spectral isomer shifts are clearly indicative of both 2+ and 3+ valence of the Eu cations with the Cu- and Au-containing compounds showing higher amounts of Eu3+ . This electronic configuration leads to an excess of negative charge in these compounds that contradicts the expected valence-precise requirement of Zintl phases. The spectra obtained at 6.5 K reveal magnetic ordering for both Eu2+ and Eu3+. The field dependence of Eu2+ indicates two distinct magnetic sublattices, with higher and lower fields, and of a small field for Eu3+. The site symmetry of the five Eu sites is not distinguishable from the Mossbauer data.