In this study, in order to examine the effects of the nanostructure of the support oxide on the reaction between alpha,beta-unsaturated aldehyde and methanol, we prepared three kinds of ceria supports for gold catalysts. The three types consisted of nano particles (CeO2-nano), rod-like particles (CeO2-rod) and cubic particles (CeO2-cube). Although the BET surface areas of these cerias correspond roughly with their estimated particle sizes, the loading of gold was the largest on CeO2-cube, which has the largest crystallite size and lowest surface area of the three oxides, and while no significant differences were found in the gold particle sizes in the TEM photographs, the surface density of gold particles was estimated to be the largest on Au/CeO2-cube. The high intensity of the (2 0 0) line compared to the (1 1 1) line in XRD diffraction implies that the (1 0 0) surface was selectively grown in the crystallites of CeO2-cube. Ce L-3-edge XANES spectra of the cerias reveal that the population of Ce(III) was larger in CeO2-nano and CeO(2-)rod than in CeO2-cube. Au 4f XPS showed that there was a higher population of Au(I) on Au/CeO2-nano and Au/CeO2-rod than on Au/CeO2-cube. In the acrolein methanol reaction, both methyl acrylate and 3-methoxy propanal were formed and comparison of the catalysts revealed that the differences in selectivity to methyl acrylate were small. In contrast, using crotonaldehyde instead of acrolein, the selectivity to methyl 2-butenoate was 100% on Au/CeO2-nano and Au/CeO2-rod and that to 3-methoxybutanal was 100% on AulCeO(2)-cube. The differences in activity and selectivity are discussed based on the structures of the catalysts and the cc,P-unsaturated aldehyde. (C) 2014 Elsevier B.V. All rights reserved.