Korean Journal of Materials Research, Vol.17, No.9, 480-483, September, 2007
SiO2 첨가량에 따른 Hydroxyapatite β-TCP 복합체의 기계적 특성
Mechanical Properties of Hydroxyapatite β-TCP Composite with Changing SiO2 Contents
E-mail:mullite999@pusan.ac.kr
Hydroxyapatites were prepared by the different addition at for 2h. With the increase of addition, microstructure, bulk density, porosity, mechanical strength of composite were investigated. When the sintered HAp contained 1 wt% , the each properties of the HAp were increased. But the excess addition of content above 1wt% the each property were decreased. This results were due to the phase. The phase appeared at 3 wt% addition and the phase was enhanced by the increasing.
  1. Langer P, Vacanti JP, Science, 260, 920 (1993)
  2. Hubbell JA, Bio-technol., 13, 565 (1997)
  3. Minuth WW, Sittinger M, Kloth S, Cell Tissue Res., 291, 1 (1998)
  4. Martin RB, Mater. Sci. Forum., 293, 5 (1999)
  5. Nunes CR, Simske SJ, Sachdeva R, Wolford LM, J. Biomed. Mater. Res., 36, 560 (1997)
  6. De With G, Van Dijk HJA, Hattu N, Prijs K, J. Mater. Sci., 16, 1592 (1981)
  7. Suchanec W, Yoshimura M, J. Mater. Res., 13, 94 (1998)
  8. Borum L, Wilson Jr. OC, Biomaterials, 24, 3681 (2003)
  9. Kim SR, Lee JH, Kim YT, Riu DH, Jung SJ, Lee YJ, Chung SC, Kim YH, Biomaterials, 24, 1389 (2003)
  10. Xu HHK, Smith DT, Simon CG, Biomaterials, 25, 4615 (2004)
  11. Sayer M, Stratilatov AD, Reid J, Calderin L, Stott MJ, Yin X, MacKenzie M, Smith TJN, Hendry JA, Langstaff SD, Biomaterials, 24, 369 (2003)
  12. Padilla S, Roman J, Sanchez-Salcedo S, Vallet-Regi M, Acta Biomater., 2, 331 (2006)
  13. Martinez A, Izquierdo-Barda I, Vallet-Regi M, Chem. Mater., 12, 3080 (2000)
트위터로 공유하기 페이스북으로 공유하기 구글플러스에 공유하기 카카오스토리에 공유하기