A lithium manganese oxide of spine! structure (LiMn2O4) has been successfully synthesised by modified sol-gel method. Two complexing agents - citric acid and acetic acid - have been utilized in order to enable a better complexing of reactants and thus better stability of reaction mixture. It results in a highly homogenous powder with satisfactory electrochemical properties. The charge/discharge tests have revealed a strong dependence of specific discharge capacities on electrode thickness. The thinnest electrodes show the lowest capacity drop while raising the discharge current from 1 C to 30 C Based on the absolute magnitude of capacity revealed by cells, the maximum specific capacity when discharged at 30 C revealed the cathode with 0.83 mg cm(-2) loading. As a result the electrode with 0.83 mg cm(-2) cathode loading possesses the best properties for construction of a high rate performance battery. (C) 2013 Elsevier B.V. All rights reserved.