Three series of solid electrolytes were prepared with the nominal compositions of (Y2 - xLi3x)Ti2O7 (Y3LT), (Y2 - xLix)Ti2O7 - x (YLT) and Y2 - xTi2O7 - 3x/2 (YT) with x = 0.040 - 0.11. Comparing the unit cell a-axis of the YLT with that of YT, the latter is shorter with the same amount of x. This indicates a successful substitution of the Li ion into the Y site of Y2Ti2O7. However, both Y3LTand YLT have exactly the same unit cell a-axis length with the same amount of x so that the solid solution formed probably has the same formula, (Y2 - xLix)Ti2O7 - x, in which only one Li ion is substituted into the Y site. Extra Li2O added in the Y3LT is probably acting as a self flux to lower the melting point of the mixture. As a result, materials become more compact and grains grow bigger. One compound of Y3LT with x = 0.060 has a total conductivity of 4.3 (4) x 10(-4) S.cm(-1) at 700 degrees C. Adding Li2O as a flux and carefully controlling the heat treatment history, compact sample of Y3LT with a relative density higher than 90% was obtained at a temperature as low as 1150 degrees C. Its ionic conductivity is comparable to one Y2Ti2O7 prepared at 1600 degrees C with a conductivity reported as 2.30 x 10(-4) S.cm(-1). (C) 2011 Elsevier B.V. All rights reserved.