Germanium is an attractive channel material for MOSFETs because of its higher mobility than silicon. In this paper, GeO2 has been investigated as an interfacial layer for high-kappa gate stacks on germanium. Thermally grown GeO2 layers have been prepared at 550 degrees C to minimise GeO volatilisation. GeO2 growth has been performed in both pure O-2 ambient and O-2 diluted with N-2. GeO2 thickness has been scaled down to approximately 3 nm. MOS capacitors have been fabricated using different GeO2 thicknesses with a standard high-kappa dielectric on top. Electrical properties and thermal stability have been tested up to at least 350 degrees C. The K value of GeO2 was experimentally determined to be 4.5. Interface state densities (D-it) of less than 10(12) CM-2 eV(-1) have been extracted for all devices using the conductance method. (C) 2012 Elsevier Ltd. All rights reserved.