Anionic polymerization was employed to synthesize well-defined diblock copolymers of polystyrene and poly(2-ethylhexylmethacrylate), PS-PEHMA. Diblock morphologies in bulk and in substrate-supported thin films were characterized by small-angle X-ray scattering (SAXS) and atomic force microscopy (AFM), respectively. PS-PEHMA diblocks exhibited thermotropic order-disorder transitions; one diblock showed a thermoreversible transition between lamellae and a higher-temperature morphology assigned as perforated lamellae. Unlike PS-poly(alkylmethacrylate) diblocks where the alkyl group is n-butyl or n-pentyl, PS-PEHMA diblocks showed a typical decreasing Flory interaction parameter with increasing temperature. Thin films of PS-cylinder-forming PS-PEHMA diblocks showed a strong preference for the cylinders to lie in the plane of the film; films of incommensurate thickness readily formed terraces. Films of commensurate thickness were easily aligned over macroscopic areas through the application of mechanical shear. (C) 2014 Elsevier Ltd. All rights reserved.